Organic Silicone Based Poly-Acrylate Binder Synthesis for Textile Pigment Printing

Sakil Mahmud, Md. Ahsan Habib, Md. Nahid Pervez, Ashraful Islam


This present study deals about an organic silicone based poly-acrylate binder by using Emulsion Polymerization technique because it produces high molecular weight polymers, and there is no or negligible content of volatile organic compounds (VOC) for textile pigment printing. The binder was prepared by polymerizing hard monomers, soft monomers, functional monomers, and compound emulsifying agent, organic silicone, an initiator, pH adjustor and deionized water. Then the properties like sublimation test, durability test, fastness test, yellowness and softness testing were performed. The role of acrylic acid and Methyl methacrylate on the characterization of the polymers was detected and recorded. A material has been selected based on pervious study of different research and effect of silicone amount on film was observed.


Poly-acrylate binder; Printing Binder; Silicon Binder; Pigment Printing; Textile Printing; Polymer Synthesis

Full Text:



Habereder P, Bereck A. Part 2: Silicone softeners. Review of Progress in Coloration and Related Topics. 2002, 32:125-137

Marchi S. Preparation and characterization of silicone nanocomposites by uv-induced hydrosilation for outdoor polymeric insulators. 2014

Bajaj P. Finishing of textile materials. Journal of Applied Polymer Science. 2002, 83:631-659

Parvinzadeh M, Hajiraissi R. Macro-and microemulsion silicone softeners on polyester fibers: Evaluation of different physical properties. Journal of surfactants and detergents. 2008, 11:269-273

Kang TJ, Kim MS. Effects of silicone treatments on the dimensional properties of wool fabric. Textile Research Journal. 2001, 71:295-300

Flesher P, Farrar D, Allen A. Thickeners used as textile pigment print paste. 1990

de Gans BJ, Duineveld PC, Schubert US. Inkjet printing of polymers: State of the art and future developments. Advanced materials. 2004, 16:203-213

Abdel-Halim E, Emam H, El-Rafie M. Utilization of hydroxypropyl cellulose and poly (acrylic acid)-hydroxypropyl cellulose composite as thickeners for textile printing. Carbohydrate polymers. 2008, 74:938-941

HUANG F, LIN Z-x. Preparation of aminosilicone oil modified core-shell structure pigment printing binder [j]. Chemistry and Adhesion. 2005, 6:007

YUAN P-r, HE H. Preparation of pigment printing binder for environmental protection [j]. Guangzhou Chemical Industry. 2006, 2:018

LIU F-f, HUANG W-j. Synthesis and characterization of a new pigment printing adhesive [j]. Textile Auxiliaries. 2005, 10:002

XIAO J-h, YU H, SONG X-y. Synthesis and characterization of environmentally friendly low temperature self-crosslinking printing binder [j]. Textile Auxiliaries. 2000, 6:007

Iqbal M. Effect of cross linking in textile pigment printing and enhancement of fastness properties. Journal of Chemical Society of Pakistan. 2009, 31:145-150

YANG Z, QUAN H. Preparation craft and application performance of polyacrylate binder for pigment printing [j]. Textile Auxiliaries. 2009, 3:011


  • There are currently no refbacks.

AJPSE(ISSN 2572-5734)Copyright © 2012-2021. All rights reserved. Published by Ivy Union Publishing, 3204 Valley Rush Dr, Apex, North Carolina 27502, United States